Silica Brick for Hot Blast Furnace

Silica brick is an acidic refractory material with good resistance to acid slag erosion. The softening temperature under load is as high as 1640-1670 °C, and the volume is relatively stable in long-term use at high temperature.
Size: as per customer's requirement
Delivery time: within 35 days after PO
Payment term: TT/LC
Packing: export fumigation wooden pallet
  • KAIYUAN

Availability:
Quantity:

Product Description

Item

Specification

SiO2 %

95

Al2O3 %

1.0

Fe2O3 %

1.3

Cold crushing strength Mpa

45

Apparent porosity %

22

Creep reate 0.2MPa 150050h %

0.8

Apparent density g/cm3 ≤

2.32

Thermal expansion 1000%

1.25

Residual quartz %

1.0

Refractoriness under load T0.6 ℃ ≥

1650


Silica bricks are made from silica≥ 96%, adding mineralizers and binders, and going through processes such as mixing, molding, drying, and sintering.

characteristic:

Silica brick is an acid refractory material with strong resistance to acid or erosion.

The high soft temperature is an excellent characteristic of silica brick, generally 1640~1680℃.

Usage:

Silica bricks are mainly used to build the carbonization chamber, combustion chamber and partition walls of coke ovens (about 73% of the refractory materials used in a coke oven are silica bricks), the kiln roof, pool walls, and high temperature load-bearing parts of hot blast stoves. , carbon roasting furnace and other thermal kilns



Previous: 
Next: 

Quick Link

Products

Zhengzhou Kaiyuan Refractories Co.,Ltd

 Plant add: Tancunwan village, Niudian town, Xinmi city, Henan, China
Export Department
 +86-13592427095 
  sales@kaiyuanref.com
        yollandahu@vip.163.com   
Send Us A Message